PU Forming Resin for Shoe Sole

1) OUT SOLE

 
테이블
ISO
POLYOL		 UFO-715P
UFO-2150R		 UFO-731PA
UFO-2310RA		 UFO-715P
UFO-2140R		 UFO-700PA
UFI-1160R		 UFO-720P
UFO-2100R
Mixing Ratio (POLYOL/ISO) 100 / 103 100 / 103 100 / 95 100 / 78 100 / 109
Viscosity
(cps)		 ISO (40℃) 200 ± 100 200 ± 100 200 ± 100 300 ± 100 400 ± 100
POLYOL(45℃) 900 ± 200 800 ± 200 900 ± 200 900 ± 200 1000 ± 200
Component
Temp(℃)		 ISO (40℃) 40 ± 2 40 ± 2 40 ± 2 40 ± 2 40 ± 2
POLYOL 45 ± 2 45 ± 2 45 ± 2 32 ± 2 45 ± 2
Mold Temp (℃) 40 - 50 40 - 50 40 - 50 40 - 50 40 - 50
Cream Time (sec) 8 - 10 6 - 8 7 - 9 8 - 10 7 - 9
Rise Time (sec) 40 - 50 30 - 40 40 - 50 43 - 55 35 - 45
Tack Free Time (sec) 45 - 55 35 - 45 45 - 55 38 - 48 25 - 30
Free Blown Den
(g/㎤)		 0.22 - 0.25 0.22 - 0.25 0.22 - 0.25 0.24 - 0.28 0.21 - 0.23
Demold Time (min) 5 - 6 3 - 4 5 - 6 5 - 7 3.5 - 4.5
Mold Density (g/㎤) 0.35 - 0.50 0.35 - 0.50 0.35 - 0.50 0,50 - 0.60 0.37 - 0.45
Hardness (Shore C) 75 - 85 75 - 85 70 - 80 70 - 80 75 - 85
Tensile Strength
(kg/㎠)		 65 - 80 65 - 80 65 - 80 80 - 100 55 - 65
Elongation (%) 350 - 450 350 - 450 400 - 500 450 - 550 350 - 450
Tear Strength (kg/cm) 20 - 30 20 - 30 20 - 30 15 - 25 15 - 25
Main Use Sandal Sandal, Casual
(Rotary System)		 Sandal, Casual
(Soft System)		 Integral Causal
 

2) MID SOLE

 
테이블
ISO
POLYOL		 UFM-770P
UFM-2700R		 UFM-770P
UFM-2790R		 UFM-780PA
UFM-2890RA
Mixing Ratio (POLYOL/ISO) 100 / 100 100 / 90 100 / 90
Viscosity
(cps)		 ISO (40℃) 500 ± 100 500 ± 100 500 ± 100
POLYOL(45℃) 1100 ± 200 1100 ± 200 1100 ± 200
Component
Temp(℃)		 ISO (40℃) 40 ± 2 40 ± 2 40 ± 2
POLYOL 45 ± 2 45 ± 2 45 ± 2
Mold Temp (℃) 40 - 50 40 - 50 40 - 50
Cream Time (sec) 8 - 10 8 - 10 6 - 8
Rise Time (sec) 55 - 65 55 - 65 55 - 65
Tack Free Time (sec) 70 - 80 70 - 80 60 - 70
Free Blown Den
(g/㎤)		 0.13 - 0.15 0.13 - 0.15 0.13 - 0.15
Demold Time (min) 5 - 6 7 - 8 3 - 4
Mold Density (g/㎤) 0.30 - 0.40 0.30 - 0.40 0.30 - 0.40
Hardness (Shore C) 50 - 65 50 - 65 50 - 65
Tensile Strength
(kg/㎠)		 20 - 35 20 - 35 20 - 35
Elongation (%) 400 - 500 400 - 500 350 - 450
Tear Strength (kg/cm) 15 - 25 10 - 15 10 - 15
Main Use - - Rotary System